Copolymerization of styrene and methacrylates in the presence of catalytic chain transfer agents (CCTAs)

Abstract

The present paper focuses on the use of a Co (II) complex [Co (afdoH) 2 (BF2) 2] as a catalytic chain transfer agent (CCTA) for controlling the molecular weight in copolymerization of styrene (STY) with butyl methacrylate (BMA) and methyl methacrylate (MMA) The catalyst is structurally similar to [Co (dmgH) 2(BF2) 2] patented by Du Pont as a CCTA Average catalytic chain transfer constant Cs of [Co (afdoH) 2(BF2) 2] for copolymerization of STY with BMA and MMA determined from Mayo plot was found to be in the range of 102–103 This value is lower than the value reported for the [Co (dmgH) 2 (BF2) 2] In the case of STYBMA or STYMMA copolymerization a considerable reduction in the viscosity average molecula r weights (MV) was observed in the copolymers The average molecular weight of poly (MMABMA) was reduced by a factor of ten compared to the reduction in poly (STYMMA) and poly (STYBMA) for the same concentration of the CCTA

سوف نركز في هذا البحث على استعمال مركب Co(II) وهو Co(afdoH)2 (BF2)2 كعامل محفز تسلسلي (CCTA) للتحكم في الوزن الجزئي للبلمرة المصاحبة لمركب الستايرين (STY) مع مركب البيوتايل ميثا إكرايلات (BMA)، ومركب الميثايل ميثا إكرايلات (MMA) إن تركيب المحفز مشابه لتركيب الـ Co (dmg–H) 2 (BF2) 2 الذي تعود براءة اختراعه لشركة دو بونت وقد وجدنا أن ثابت المحفز التسلسلي للمركب {Co (afdo–H) 2 (BF2) 2 للبلمرة المصاحبة للستايرين (STY) مع مركب BMA ومركب MMA باستعمال بيانات ”مايو“ يقع ضمن المجال (102103) وهذه القيمة أقل من القيمة المعروفة بالنسبة Co (dmgH)2 (BF2) 2 كما وجدنا أيضا أنه في حالة البلمرة المصاحبة STYMMA أو STYBMA فإن متوسط الوزن الجزئي (باستخدام طريقة اللزوجة) قد تناقص بصورة ملحوظة، ومتوسط الوزن الجزيئي لبولمر (MMABMA) قد تناقص عشرة أضعاف مقارنة مع التناقص الحاصل في بوليمر (STYBMA) و(STYMMA) عند نفس تركيز CCTA