Chloride diffusion coefficient of concrete in the Arabian Gulf environment

Abstract

This investigation evaluates the chloride diffusion coefficient for concrete made with marginal limestone aggregates and Type V Portland cement commonly used in the Arabian Gulf Parameters investigated are (1) watercement ratio (2) cement content (3) surface chloride concentration and (4) exposure condition An attempt is made to arrive at a model for predicting the onset of corrosion using the limited test data The experimental results revealed that the chloride diffusion coefficient is strongly influenced by water cement ratio and exposure conditions and marginally by cement content but unaffected by the surface chloride concentration The chloride diffusion coefficient values ranged from (8 to 170) x 108 cm2 sec for different concrete mixes and exposure conditions The high value of the chloride diffusion coefficient is mainly attributed to the low concrete quality and the local aggressive environmental conditions The basis of the prediction model to corrosion initiation has been set and reasonable results are produced based on the limited experimental data

يقيم هذا البحث عامل انتشار أيون الكلوريد في الخرسانة المصنوعة من الركام الجيري والإسمنت البورتلاندي المقاوم للسلفات التي تستعمل بكثرة في منطقة الخليخ العربي تم دراسة المتغيرات التالية نسبة الماء للإسمنت، كمية الإسمنت تركيز نسبة الكلوريد على سطح الخرسانة، الأجواء المحيطة ومن ثم محاولة إيجاد علاقة رياضية للتنبؤ ببداية صدأ الحديد التسليح اعتمادا على اتنشار أيون الكلوريد في الخرسانة لقد حددت قيمة عامل الانتشار بين 1708 × 10 سم ثانية لخلطات خرسانية وأجواء محيطية مختلفة إن هذه القيم العالية لعامل انتشار يمكن غزوها إلى رداءة نوعية الخرسانة وصعوبة الأجواء المحلية المحيطة لقد تم وضع حجر الأساس لإمكانية تنبؤ بداية صدأ حديد التسليح والتي قد أعطيت نتائج مجدية نسبية إلى المعطيات المحدودة من هذه التجارب