Measurement of fatigue cracks by nondestructive testing مراقبة شروخ الكلال بوساطة الاختبارات غير المتلفة

Abstract

Detection of cracks in metallic specimens subjected to fatigue loading by nond estructive inspection techniques is demonstrated In the experimental phase of this study standard rod specimens were fatigue loaded The tests were performed at different constant stress amplitudes at room temperature To measure crack size the specimens were removed from the testing machine after certain number of load cycles and were nondestructively inspected via ultrasonic eddy current and Xray techniques In this way a measure of the crack width and depth as function of the applied load level and number of cycles was obtained A brief review of the methods of nondestructive inspection of fatigue cracks is also given Advantages and disadvantages of the different inspection techniques are discussed It is concluded that the ultrasonic inspection is the most reliable method

تمت في هذا البحث عملية الكشف عن الشروخ الناتجة في عينات معدنية خاضعة لأحمال كلال، وذلك بطرق الكشف غير المتلفة وقد تمت التجارب على عينات قياسية من الألومنيوم تم إخضاعها لأحمال كلال مختلفة القيمة تحت ظروف درجة حرارة الغرفة ولمراقبة نمو الشروخ، تمت بالموجات فوق الصوتية، والكشف بالتيارات الدوامية، والكشف بالأشعة السينية وتم بهذه الطرق قياس عرض وعمق الشروخ كدالة لمقدار الحمل وعدد دورات التحميل كما تمت في هذا البحث أيضا مراجعة طرق الاختبار غير المتلف في الكشف عن الشروخ الناتجة من الكلال، وتمت مناقشة مزايا ومساوئ كل طريقة ونتيجة لذلك، فقد تم التوصل إلى أن طريقة الكشف بالموجات فوق الصوتية هي الطريقة الأكثر اعتمادية من باقي طرق الكشف غير المتلف