Chemical composition of cements produced in Saudi Arabia and its influence on concrete strength التركيب الكيميائي للإسمنت المنتج في المملكة العربية السعودية وتأثيره على قوة الخرسانة

Abstract

In this research project the variability of chemical composition of cements produced in the Kingdom and its impact on the strength development of concrete up to 5 years were investigated The test results showed that the chemical composition of Type I cement produced in the Kingdom is similar to typical values of Type I cement in the literature However the Type V cement demonstrated high C3S and low C2S contents It was also found that all cements have low amount of alkali equivalent which can be classified according to ASTM C150 as lowalkali cement The results of compressive strength of concrete made with Type I cement were 24 MPa higher than corresponding concrete made with type V cement at all ages up to 5 years

يتجاوز استهلاك الإسمنت في المملكة العربية السعودية في الوقت الحالي 25 مليون طن في السنة، ويعد معدل استهلاك الفرد في المملكة من أعلى المعدلات في العالم يبلغ عدد شركات الإسمنت العاملة في المملكة ثمان شركات بطاقة إنتاجية تصل إلى 22 مليون طن في السنة وهناك خطط لفتح مصانع إسمنت جديدة وتوسع كبير في المصانع القائمة وهذا سيؤدي إلى زيادة الطاقة الإنتاجية الحالية إلى الضعف تم في هذا البحث دراسة تأثير متغيرات التركيب الكيميائي للإسمنت المنتج في المملكة وتأثيره على قوة الخرسانة مع الزمن حتى عمر خمس سنوات بينت نتائج الاختبارات أن التركيب الكيميائي للنوع الأول للإسمنت المنتج في المملكة مشابه للنوع الأول للإسمنت الموجود في الأدبيات العالمية، ولكن النوع الخامس كان مختلفا في قيم C2S وC3S كما وجد أنه بالإمكان تصنيف الإسمنت المستخدم في هذه الدراسة وفقا للـ ASTM C150 على أنه إسمنت ذو وسط قاعدي منخفض (low alkali cement) أظهرت نتائج قوة الضغط للخرسانة المصنعة باستخدام النوع الأول للإسمنت أنها أعلى بحوالي 2 إلى 4 نيوتن مم 2 مقارنة بالخرسانة المصنعة باستخدام النوع الخامس عند كل الأعمار حتى خمس سنوات