The dielectric behaviour of graphite doped BaTiO3 خواص العزل الكهربي لمركب تيتانات الباريوم المضاف إليه نسب صغيرة من الجرافيت
Authors:
Issa Mohamed Ali A Molokhia Nabil Mahmoud
Issue Date:
1978
Citation:
The dielectric behaviour of graphite doped BaTiO3 خواص العزل الكهربي لمركب تيتانات الباريوم المضاف إليه نسب صغيرة من الجرافيت N M Molokhia and M A A IssaJournals of Faculty of Science Riyadh UniversityVol 9 (1978) p p 207216Molokhia Nabil MahmoudIssa Mohamed Ali A
Abstract:
The effect of adding 001 to 5 wt % of graphite on the dielectric properties loss tangent and d c resistivity of sintered barium titanate was investigated at different temperatures The dielectric constant has been sharply decreased with increasing the graphite percentage In the loss tangent versus temperature curves a discontinuity was noticed at the cubictetragonal transition temperature It disappeared when a d c voltage of 10 volts was applied superimposed on the a c measuring voltage Such anomaly has been explained as due to some sort of switching process in the material Increasing the graphite contents shows an increase in the resistivity of the system up to a percentage of 1 % graphite and then decreased again The resistivity versus temperature curves show peak values at nearly 80 C for the different percentages تمت دراسة خواص العزل الكهربي والفقدان والمقاومة النوعية عند درجات حرارة مختلفة لمركب تيتانات الباريوم مضافا إليه نسب صغيرة من الجرافيت تتراوح بين 010 % إلى 5 % وقد لوحظ أن ثابت العزل قد انخفض انخفاضا ملحوظا بإضافة الجرافيت إلى تيتانات الباريوم كما لوحظ وجود نقطة انقلاب في منحنى الفقدان مع درجة الحرارة وذللك عند درجة الحرارة وذلك عند الدرجة الانتقالية وقد اختفت هذه الظاهرة عندما أضيف فرق جهد ثابت مقداره 10 فولت مع فرق الجهد المتردد الذي أجريت القياسات عنده وقد نوقشت هذه الظاهرة مع ظاهر زيادة المقاومة النوعية بزيادة نسبة الجرافيت من صفر إلى 1 % وقد لوحظ وجود نهاية عظمى في منحنيات تغير المقاومة بتغير درجة الحرارة وذلك عند 80 م تقربيا لجميع النسب