Effect of dislocation density on the activation of recovery of coercive force for a ferromagnetic material
المؤلفون:
Tan Doa Van Kassem Mohamed Emad
تاريخ النشر:
1977
الاستشهاد المرجعي :
Effect of dislocation density on the activation of recovery of coercive force for a ferromagnetic material Doa Van Tan and Mohamed Emad KassemThe Arabian journal for science and engineering المجلة العربية للعلوم والهندسة Univeristy of Petroleum and MineralsVol 2 no 2 (May 1977) p p 6975Tan Doa VanKassem Mohamed Emad
الملخص:
The applicability of the theory of the recovery of coercive force after plastic deformation of a ferromagnetic material has been investigated It is found that the results obtained for the ferritic stainless steel 1× 0 CrA1 24 are in good agreement with the theory discussed The activation energy of the recovery process is found to be reduced on increasing the degree of plastic deformation Also the deformation texture and the dislocation structure playa dominant role in the recovery process يهتم هذا البحث بدراسة استرجاع قوة الممانعة المغناطيسية (Coercive force) بالمعالجة الحرارية لأحد المواد الفرومغناطيسية بعد تعرضها للتشوه اللدن (Plastic Deformation) واختبار مدى تطابق النتائج المعملية مع العلاقات النظرية التي تناقش هذه المشكلة ولقد أظهرت نتائج هذه الدراسة ما يلي (1) إن النتائج المعملية تتطابق إلى حد بعيد مع النظرية المراد اختبارها في شأن انخفاض قوة الممانعة المغناطيسية بالمعالجة الحرارية المصلب الغريتي (x10 Cr AI 24) بعد تعرضه للإجهاد اللدن (2) إن طاقة التفاعل اللآزمة لعملية التفاعل تتناقص بتزايد درجة التشوه اللدن للعينات المختبرية (3) إن طاقة التفاعل تتغير مع درجة التشوه اللدن بصورة غير عادية في صورة خط مستقيم منكسر، حيث لوحظ تناقص فجائي كبير في طاقة التفاعل عندما تخطت درجة التشوه اللدن 30 % (4) إن النسيج التشوهي (Deformation Texture) والتركيب البنائي للانخلاعات (Dislocation Structure) يلعبان دورا محسوسا في عملية الاسترجاع