Influence of additives in a H SO environment on the stress corrosion cracking of type 304 stainless steel

Abstract

This study evaluates the resistance of type 304 stainless steel to stress corrosion cracking in sulfuric acid solutions with after addition of potassium cyanate potassium selenocyanate decomposition products of cyanate (NH OH NaHCO or (NH ) CO ) and NaOH Cracking or localized attacks occurred at sulfate ion concentrations of 154 M and at pH values less than 035 The results show that addition of KOCN NH4OH NaHCO3 and (NH ) CO cause cracking to predominate by inhibiting general corrosion both by neutralization of some of the aggressive H ions and by adsorption of these species on the metal surface KSeCN induces localized attack but inhibits general corrosion through adsorption NaOH induces SCC by its inhibitive effect decreasing the H ion concentration

تقييم هذه الدراسة مقاومة الحديد المانع للصدأ من نوع (304) لترشحات إجهاد الصدأ في محلول حمض الكبريتيك بعد إضافة سينيت البوتاسيوم، وسلينوسينيت البوتاسيوم، مركبات سينيت التحللية (NH OH NaHCO أو (NH ) CO ) وNaOH وتحدث الشروخ أو الآثار المحلية عند تركيز أيونات الكبريتات الذي يتراوح بين (15) إلى (40) M وعند قيمة للرقم الهيدروجيني PH تساوي أقل من (035) تشير النتائج إلى أن إضافة KOCN NH4OH NaHCO3 (NH ) CO تسبب طغيان الشورخ يمنع الصدأ العام بواسطة معادلة بعض أيونات الهيدروجين الضارة وكذلك بادمصاص هذه المجموعات على سطح المعدن كما يتسبب KSeC في أثار محلية ولكن يمنع الصدأ العام وذلك بواسطة الادمصاص ويؤدي NaOH إلى SCC وذلك عن طريق تأثير المانع مقللا تركيز أيونات الهيدروجين