Hydrogen supersaturation effects in zirconium and its alloys during electrochemical hydriding
Auteur(s):
Walton G N Rashid M
Date de publication:
1983
Référence bibliographique:
Hydrogen supersaturation effects in zirconium and its alloys during electrochemical hydriding M Rashid and G N WaltonThe Arabian journal for science and engineering المجلة العربية للعلوم والهندسة Univeristy of Petroleum and MineralsVol 8 no 1 (January 1983) p p 38Rashid MWalton G N
Résumé:
During electrochemical investigations on the hydriding behavior of zirconium
zircaloy 2 and zircaloy 4 in 10 N H2 S04 aqueous solution calculations were made
on the ratio of gram atom hydrogen to gram atom metal (H m) H m values increased
linearly with time of cathodic treatment and finally tended to attain a
plateau with H m values as high as 95 This value is much higher than can be
explained if only hydride formation is assumed to take place and indicates supersaturation
effects which may be significant for application in the use of metals for
hydrogen storage أثناء الدراسات على الهدرجة الإلكتروكيميائية لمعدن الزركونيوم وسبائكه رقم 2 و4 في محلول مائي معياري لحامض الكبريتيك قمنا بحسابات للقيمة (Hm) وهي نسبة الجزيء الغرامي للهيدروجين لكل جزيء غرامي من المعدن تزداد قيم (Hm) ازديادا خطيا مع زمن معالجة الكاثود إلى أن تصل إلى هضبة تتوقف قيمة فيها عن الازدياد وتصل قيمة (Hm) فيها إلى 95 هذا الرقم العالي لقيمة (Hm) لا يمكن تفسيره بافتراض الهدرجة لوحدها ويدل أن ظواهر الإشباع تلعب دورا هاما يجعلها ذات منفعة عملية لتخزين الهيدروجين