Kinetics of hydrogenation of furfural to furfuryl alcohol over copper chromite catalyst and optimum regeneration procedures
المؤلفون:
Dogu Timur Soner Eyup Yorulmaz Yavuz
تاريخ النشر:
1996
الاستشهاد المرجعي :
Kinetics of hydrogenation of furfural to furfuryl alcohol over copper chromite catalyst and optimum regeneration procedures Eyup Soner Timur Dogu and
Yavuz YorulmazThe Arabian journal for science and engineering المجلة العربية للعلوم والهندسة Univeristy of Petroleum and MineralsVol 21 no 2 (April 1996) p p 321332Soner EyupDogu TimurYorulmaz Yavuz
الملخص:
The deactivation mechanism of a copper chromite catalyst used in selective
hydrogenation of furfural to furfuryl alcohol was investigated and the methods to
regenerate it were searched The catalyst deactivation mechanisms was found to be
due to the fouling resin macromolecules formed by side reactions of furfural on
the catalyst surface The optimum catalyst regeneration was by one drying at
1100 e for 5 days heating at 325 C for 18 hours followed by refluxing in
cyclohexanol for 4 hours The conversion to furfuryl alcohol by the regenerated
sample in vapor phase hydrogenation was 78 per cent compared to 795 per cent
for the fresh catalyst
The following rate equation for hydrogenation reaction under investigation was
derived from experimental results
dXA dt 3837 (1XA) 38 تبحث هذه الدراسة في ميكانيكية التخميد لحفاز النحاس الكرومي والمستخدمة في الهدرجة الانتقائية للفروفرال إلى كحول الفروفريل، كما وتبحث أيضا في طرق إعادة هذا الحفاز وجدنا أن الجزئيات الكبيرة الناتجة عن التفاعلات الجانبية للفروفرال والمترسبة على أسطح الحوافز تعمل على تعطيل هذه الحفازات كما وجدنا أن أفضل طريقة لتخميد هذه الحفازات يكون بتجفيفها عند درجة حرارة 110 م لمدة خمسة أيام، ثم تسخينها عند درجة حرارة 325 م لمدة (18) ساعة، ويتبع ذلك إعادة تذويبها بـ(سيكلوهكسانول) لمدة أربع ساعات أظهرت الحفازات المعالجة بالتبخير كفاءة قدرها 78 % مقارنة بـ 795 % للحفازات الجديدة