Xray photoelectron spectroscopy investigation of sodiumditellurate glasses
Auteur(s):
Hussain Z
Date de publication:
1990
Référence bibliographique:
Xray photoelectron spectroscopy investigation of sodiumditellurate glasses Z Hussain [et al]The Arabian journal for science and engineering المجلة العربية للعلوم والهندسة Univeristy of Petroleum and MineralsVol 15 no 2B (April 1990) p p 337343Hussain Z
Résumé:
XRay photoelectron spectroscopy study of sodiumditellurate glasses containing chromium oxide reveals that the ratio between bridging and nonbridging oxygen is unaffacted by the addition of Cr O in small quantities This observation is in agreement with the IR study reported earlier A small quantity (about 10%) of a nondecomposed component of Na2C03 has been detected in the glass which is in contradiction with the general expectation that the Na2CO3 in the glass melt decomposes to Na2O and CO2 تشير دراسة مطياف الانبعاث الكهرضوئي باستخدام الأشعة السينية في زجاج ثاني تاليوريت الصوديوم والذي يحتوي على مادة الكروميوم بأن النسبة بين ذرات الأكسجين القنطرية الربط وغير القنطرية الربط لا تتأثر بإضافة كميات قليلة في أكسيد الكروميوم (Cr O )
وتتفق هذه الظاهرة مع دراسات سابقة لمطيافية الأشعة تحت الحمراء وقد وجد أن كمية ضئيلة من كربونات الصوديوم (Na2CO3) قرابة (10%) لا تتحلل بل وتبقى على هيئتها في الزجاج خلافا لما هو متوقع عادة، وبأن كربونات الصوديوم تتحلل في مصهور الزجاج إلى أكسيد الصوديوم (Na2O) وثاني أكسيد الكربون (CO2)