Potential criteria for cathodic protection of steel in concrete simulated environment
Auteur(s):
Thangavel K Balakrishnan K Rengaswamy N S
Date de publication:
1989
Référence bibliographique:
Potential criteria for cathodic protection of steel in concrete simulated environment K Thangavel N S Rengaswamy and K BalakrishnanThe Arabian journal for science and engineering المجلة العربية للعلوم والهندسة Univeristy of Petroleum and MineralsVol 14 no 2 (April 1989) p p 357363Thangavel KRengaswamy N SBalakrishnan K
Résumé:
Potentiostatic studies were made in aqueous alkaline media representing
different concrete environmental conditions pH 8 10 11 and 124 using aqueous
sodium hydroxide solutions Chloride and sulfate concentrations in the above
solutions were varied from 100 to 35000 ppm
Open circuit potential of steel in such simulated concrete environments was
found to lie in the range300 to600 m V versus SCE Though shifting the
potential to00 mV was found to give complete cathodic protection a potential
of800 mV versus SCE was found to be desirable عملت دراسات باستخدام فرق الجهد لحديد التسليح في محاليل قلوية والتي تحاكي الظروف البيئية القلوية المختلفة للخرسانة تكون فيها قيم درجة الحموضة (PH) تساوي 8، 10، 11، 124 ولقد حضرت هذه المحاليل باستخدام محلول هيدروكسيد الصوديوم وكانت نسبة مواد الكلوريد والكبريتات في هذه المحاليل تترواح من 100 إلى 35000 جزء في المليون ولقد أظهرت هذه الدراسة أن فرق الجهد المفتوح للحديد الموضوع في هذه المحاليل يكون بين (300) إلى (600) ملي فولت، كذلك أظهرت الدراسة أن تحويل القيمة إلى (700) ملي فولت أعطى الحديد حماية كاثودية ووجد أن أنسب قيمة لذلك هي (700) ملي فولت