From crystal to amorphous transformation in Hf63Pd37 system prepared by mechanical alloying من الشكل البلوري إلى الشكل غير المحدد في مركب (Hf63Pd37) المعد بالخلط المعدني الميكانيكي

Abstract

The structural transformation from crystalline structure to amorphous structure of HfPd system prepared by mechanical alloying (MA) technique was investigated Xray diffraction technique was used to study structural changes with MA time Differential scanning calorimetry (DSC) was used to study the stability of the resulting amorphous HfPd phase A direct transformation from crystalline to amorphous phase was observed The density of the crystalline peaks of both the hexagonal Hf and cubic Pd phases decayed exponentially as a function of the milling time The time constants of the decaying process were obtained On an atomic scale the radial distribution function RDF(r) and the thermal behavior of the MA Hf63Pd 37 (milled for 6 h) showed that it is of a single amorphous phase

لقد تم بحث تحولات البنية في نظام HfPd، المعد بطريقة السبك الميكانيكي، خلال تحوله من البنية الأمورفية (اللاشكلية) تم استخدام حيود الأشعة السينية لدراسة التغيرات في البنية كدالة في زمن السبك الميكانيكي كذلك استخدم جهاز الماسح الحراري التفاضلي (DSC) لدراسة الاتزان الحراري للطور الأمورفي الذي تم استخلاصه لقد كان التحول من البنية البلورية إلى البنية الأمورفية، مباشرا، وقد لوحظ أن شدة الأشعة السينية للطورين البلوريين السداسي والمكعب انخفضت على شكل دالة أسية تناقصية، وقد تم اشتقاق الثوابت الزمنية لهذين الطورين ومن جانب آخر، فقد تم إثبات أن البنية الأمورفية لـ Hf63 Pd37 الناتجة بعد 6 ساعات من السبك الميكانيكي وحيدة الطور، وذلك من خلال السلوك الحراري ودراسة دالة التوزيع نصف القطرية (RDF) لهذه العينة