Kinetic analysis of nonisothermal decomposion of (Mg5 (Co3)4 (OH)2 4H2O 5 CR2O3) crystalline mixture التحليل الحركي للانحلال عند تغير درجات الحرارة للخليط البلوري (Mg5 (CO3)4 (OH)2 4H2O 5 CR2O3)

Abstract

Pure MgCR2O4 spinel was synthesized from crystalline mixure of (Mg5 (CO3)4 (OH)2 4H2O 5 Cr2O3) by heating at 900 C for 27 h TG DTA FTIR and XRPD techniques were used to follow the reactions and identify the products Nonisothermal kinetics of thermal decomposition of unirradiated and yirradiated physical crystalline mixtures were studied in static air The kinetic parameters were obtained through modelfitting and modelfree methods and artificial isokinetic relationship (IKR) for multistep processes The results show that the decomposition for both unirradiated and yirradiated mixures proceed through two steps with different reaction mechanisms The first is a thirdorder reaction (F3) mechanism followed by onedimensional diffusion (D1) as a second step

تم تحضير سبينل نقي من رفع درجة حرارة الخليط البلوري (Mg5 (CO3)4 (OH)2 4H2O 5 CR2O3) عند 900 C لمدة 27 ساعة استخدمت تقنيات TG وDTA وFTIR وXRPD لتتبع التفاعل والتعرف على النواتج تم دراسة حركية الانحلال الحراري عند تغير درجات الحرارة للخليط البلوري الفيزيائي غير المشعع والمشعع في الهواء الثابت وتقدير الدوال الحركية من خلال تقريبات النماذج المقيدة والحرة وعلاقة ثبوت الحركية للعمليات عديدة الخطوات (IKR) أظهرت النتائج أن انحلال الخليطين (غير المشعع والمشعع) يتم بخطوتين متتابعتين بميكانيكيتين مختلفتين الأولى ميكانيكية التفاعل من الرتبة الثالثة (F3)، والثانية ميكانيكية الانتشار في بعد واحد (D1)