Electrochemical characterization of heat treated steel دراسة كهروكيميائية للحديد المعالج حراريا
المؤلفون:
Al Odan Maher Abd Allah Al Ghonamy Abd El aziz Ibrahim
تاريخ النشر:
2008
الاستشهاد المرجعي :
Electrochemical characterization of heat treated steel دراسة كهروكيميائية للحديد المعالج حراريا Abdulaziz AlGhyamah and Maher Al Odanمجلة جامعة الملك سعود مجلة العلوم الهندسية عمادة شؤون المكتبات، جامعة الملك سعودVol 20 no 1 (1429 H 2008) p p 6168Al Ghonamy Abd El aziz IbrahimAl Odan Maher Abd Allah
الملخص:
Different steel alloys of tool steel and alloy steel were heat treated with different heat treatment processes such as hardening gas carburizing and gas nitriding The electrochemical behavior especially corrosion characteristics of the different steel grades were evaluated using different electrochemical techniques in 01 M sodium chloride solutions at different values of solution pH Potentiodynamic scans indicated similar corrosion behavior between the different heat treatment processes However the nitriding process added extra corrosion resistance to certain steel alloys which included strong nitride forming elements Also the electrochemical impedance spectroscopy and salt spray tests confirmed the same and indicated an increase in corrosion resistance after the nitriding process يهدف هذا البحث إلى دراسة تأثير بعض عمليات المعالجة الحرارية والسطحية مثل الكربنة، والنتردة، والتقسية على الخواص الكهروكيميائية لبعض سبائك الحديد تم تقييم تآكل هذه السبائك وتصرفها الكهروكيميائي باستخدام المحلول المائي لملح الطعام بتركيز 01 مولار عند ظروف مختلفة من الرقم الهيدروجيني دلت نتائج البحث على تشابه الأنواع المدروسة للمعالجة الحرارية من ناحية نتائج التآكل، لكن عملية النتردة أدت إلى زيادة مقاومة التآكل في سبائك معينة للحديد